In the process of composite electroplating galvanized wire, the plating solution must be stirred to obtain the composite coating in which the particles dispersed in the matrix metal. Stirring methods include mechanical stirring, air stirring, ultrasonic stirring, bath circulation, etc. The acid activation solution in the production process can remove the corrosion products and oxide film on the surface of the low carbon steel wire without excessive corrosion on the matrix.

Because of the large size of the  barbed rope, the rope factory is used to packing. If you do not pack, then a load of blade rope can not hold many pieces, but also relatively occupy space and easy to be lost in the process of transportation.

Iron and steel in the condition of cooling on the surface galvanized, and hot dip galvanized steel pipe in the condition of hot dip on the surface, its adhesion is strong, not easy to fall off, hot dip galvanized pipe although also rust phenomenon, but in a long period can meet the technical and sanitary requirements.

Stainless steel material refers to air, steam, water and other weak corrosive medium and acid, alkali, salt and other chemical corrosion medium corrosion of steel, also known as stainless acid steel. In practical application, the steel with weak corrosion resistance is often called stainless steel, and the steel with chemical corrosion resistance is called acid resistant steel. And galvanized wire has good toughness and elasticity, zinc can reach 300 grams/square meter. It has the characteristics of thick galvanized layer and strong corrosion resistance. Products are widely used in construction, handicrafts, silk screen preparation, highway guardrail, product packaging and daily civil and other fields.

1. Zinc pot operators must stick to their posts

Strictly control the pH value of large roll galvanized wire bath, research shows that the size of the bath pH value directly affects the quality of steel wire coating, improper control of pH value will cause loose coating. When the pH value is greater than 3, the steel wire coating has burr caused by fine dendrites, and the surface is not smooth. The current density is strictly controlled. From the microscopic morphology, the higher the current density, the larger the zinc layer grain deposition, the less dense the corresponding zinc layer.