Large roll galvanized wire phosphating film is dark gray to black gray, the thickness is generally 5-20μm, has better corrosion resistance in the atmosphere. Membrane is a microporous structure, strong adsorption ability to paint, such as used as paint bottom, corrosion resistance can be further advanced. Metal oxidation treatment: Add steel products to NaOH and NaNO2 mixed solution, heating treatment, the surface can form a layer of thickness of about 0.5-1.5μm blue oxide film, in order to reach the purpose of steel corrosion prevention, this process is called blue treatment, referred to as blue.

Post time: 23-09-22

Post time: 05-05-23

First, the effect of tensile strength or hardness of steel wire

Cold galvanizing, also called electric galvanizing, is the use of electrolytic equipment to remove oil, pickling, after the pipe fitting into the composition of zinc salt solution, and connected to the negative electrode of the electrolytic equipment. Wire factory on the opposite side of the pipe fittings placed zinc plate, connected to the positive electrode of the electrolytic equipment is connected to the power supply, the use of current from the positive electrode to the negative electrode will deposit a layer of zinc on the pipe fittings, cold plating pipe fittings is first processed after galvanized.

Wire rod to stop normalizing or soxaustenitizing treatment, large specifications with spheroidizing annealing instead. In the middle, especially before the waste product drawing process of thermal disposal throughout the selection of soxaustenitizing disposal. Decarbonization should be prevented during thermal disposal. Sulfuric acid or hydrochloric acid pickling was used to remove the oxide sheet after hot treatment. Coating (see lubrication carrier) can be dipped in lime, phosphating, borax disposal or copper plating.

Therefore, when zinc reaches saturation in the solid melt, the two elements of zinc and iron atoms diffuse with each other, and the zinc atoms diffused into (or infiltrated into) the iron matrix migrate in the lattice of the matrix and gradually form an alloy with iron, while the iron diffused into the molten zinc liquid forms an intermetallic compound FeZn13 with zinc and sinks into the bottom of the hot-dip galvanized pot, that is, zinc slag. When the workpiece is removed from the zinc leaching solution, the surface of the pure zinc layer is formed, which is hexagonal crystal, and its iron content is not more than 0.003%.

In addition, the corrosion resistance of hot-dip galvanized wire will also be affected by other factors. For example, in different environments, especially in some special chemical environments, such as acidic or alkaline environments, the corrosion resistance of hot-dip galvanized wire may be affected to a certain extent. At this time, it may be necessary to use other materials that are more resistant to corrosion to replace the hot-dip galvanized wire.

According to the galvanized iron wire manufacturer, galvanized iron wire is the selection of excellent low carbon steel, through drawing forming, pickling rust removal, high temperature annealing, hot dip galvanized, cooling and other processes. Galvanized iron wire should pay attention to the following points in the use process:

Post time: 07-04-23

There are many production links of blade barbed rope, and the finished product can only be produced after several times of production. Roughly, there are four or five links.

2, the production and installation is simple and fast, the use of patented friction connection or special connection accessories for installation, greatly improve the installation efficiency.

The surface of alluvium before hot dip galvanizing of orchard special electric galvanized shaft wire can partially remove the surface film layer, surface impurity and other shortcomings according to the basic technology to find and solve; Excessive foam is caused by soap and soapable surface active substances such as human fat into the tank. A moderate rate of foam production would be fine. There are many fine homogeneous particles in the tank, can stabilize the foam layer, with activated carbon mat to remove surface active substances. Or make the bubble unstable according to overworry, these are all reasonable countermeasures; Other strategies should also be used to reduce the amount of surface-active substances introduced. The introduction of organic matter can make the electroplating process speed drop sharply. Although the secret recipe of organic chemistry is beneficial to the high accumulation rate, the thickness of the coating can not meet the requirements after the organic matter is brought in, so the activated carbon can be used to solve the tank.

2. Eliminate caked zinc residue on zinc liquid surface

Angular Contact Ball Bearings Product Guide and Specifications Overview

28580 bearing

weizi bearing bearing ball deep groove

Roulements à contact angulaire - Performance et Précision

weizi bearing bearing pressing machine

weizi bearing cylindrical roller bearing supplier

weizi bearing nj 206 bearing

weizi bearing 23244 bearing

Design and Applications of Single Thrust Ball Bearings in Machinery Systems